WC-10Co4Cr Thermal Spray Poeder
- Sawol Agglomerated & Sintered en Sintered and Crushed poeder binne beskikber. Agglomerearre en sintere poeders binne bolfoarmich as hast sfearysk mei goede streamberens. Sintered en gemalen poeders binne unregelmjittich.
- De maksimale tsjinsttemperatuer is oant 500 ℃.
- De dichte coating hat hege hurdens mei poerbêste wjerstân tsjin abrasive wear, fretting wear, adhesive wear, en eroazje wear.
- It ferfangen fan hurde chrome plating.
- Kobalt & Chrome hat bettere korrosjebestriding en slijtageeigenskippen dan kobalt, benammen yn wiet- en korrosjeomjouwings.
- Benammen brûkt yn fleantugen lâningsgestel, poarte kleppen, bal kleppen, papier rollers, hydraulyske silinders, compressor stangen, metallurgyske rollers, meganyske dielen, ensfh
Grade & gemyske gearstalling
Klasse |
Gemyske gearstalling (Wt, %) |
|||||
W |
T.C |
Co |
Cr |
Fe |
O |
|
ZTC45 |
Lykwicht |
5.2 – 6.0 |
9.1 – 10.1 |
3.0 – 4.5 |
≤ 1.0 |
≤ 0,5 |
ZTC45D* |
Lykwicht |
5.2 – 6.0 |
9.1 – 10.1 |
3.0 – 4.5 |
≤ 0,15 |
≤ 0,5 |
*: D stiet foar sferysk of near-sfearysk thermysk spuitpoeder.
Spesifikaasje & Fysike eigenskippen
Klasse |
Type |
Grutte fraksje (μm) |
Skynbere tichtens (g/cm³) |
Flow Rate (s/50g) |
Oanfraach |
ZTC4551 |
WC - Co - Kr 86/10/4 Sintered & Crushed |
– 53 + 20 |
≥ 4 |
≤ 25 |
(JP5000 & JP8000, DJ2600 & DJ2700, JetKote, Woka Jet, K2)
|
ZTC4553 |
– 45 + 20 |
≥ 4 |
≤ 25 |
||
ZTC4552 |
– 45 + 15 |
≥4 |
≤ 25 |
||
ZTC4551D |
WC - Co - Kr 86/10/4 Agglomerearre & Sinter |
– 53 + 20 |
≥ 4 |
≤ 18 |
|
ZTC4553D |
– 45 + 20 |
≥ 4 |
≤18 |
||
ZTC4552D |
– 45 + 15 |
≥ 4 |
≤18 |
||
ZTC4581D |
– 45 + 11 |
≥ 4 |
≤18 |
||
ZTC4554D |
– 38 + 10 |
≥ 4 |
≤18 |
||
ZTC4582D |
– 30 + 10 |
≥ 4 |
≤ 18 |
||
Wy kinne ferskillende partikelgrutte distribúsjes en skynbere tichtheden op maat meitsje foar ferskate tapassingen. |
Oanrikkemandearre spuitparameters (HVOF) |
|
Coating Eigenskippen |
||
Materiaal |
WC - 10Co - 4Cr |
|
Hardheid (HV0.3) |
1150 – 1400 |
Manufacturing |
Agglomerearre & Sintered |
|
Bonding Strength (MPa) |
> 70 MPa |
Grutte fraksje ( µm ) |
– 45 + 15 |
|
Deponearre effisjinsje (%) |
40 – 55% |
Spray fakkel |
JP5000 |
|
Porositeit (%) |
< 1% |
Nozzle (inch) |
6 |
|
|
|
Kerosine (L/h) |
24 |
|
||
Oxygen (l/min) |
944 |
|
||
Dragergas (Ar) (L/min) |
7.5 |
|
||
Poeder feed rate (g/min) |
70 – 80 |
|
||
Spuitafstand (mm) |
340 – 380 |
|