Cr3C2-37WC-18NiCoCr Thermal Spray Powder
- Agglomerated and Sintered gray-black spherical or near-spherical particles.
- The maximum service temperature is up to 700℃.
- The coating has excellent resistance to sliding wear, abrasive wear, erosive wear, corrosive wear, cavitation, and corrosion.
- Excellent resistance to solid, liquid, and gas corrosion in elevated temperatures.
- Excellent resistance to high-temperature complex corrosion.
Mainly used in pump valve parts, power generation boilers, biomass-burning boilers, the chemical
Grade & Chemical Composition
Grade |
Chemical Composition (Wt, %) |
||||||
W |
T. C |
Co |
Ni |
Cr |
O |
Fe |
|
ZTC49D* |
Balance |
7.8 – 8.4 |
3 – 4 |
10.5 – 12.5 | 39.5 – 42.5 |
≤ 0.5 |
< 0.5 |
*: D stands for spherical or near-spherical thermal spray powder.
Size & Physical Properties
Grade |
Type |
Size Fraction (μm) |
Apparent Density ( g/cm³) |
Flow Rate (s/50g) |
Application |
ZTC4951D |
Cr3C2 – WC – NiCoCr 45/37/18 Agglomerated & Sintered |
– 53 + 20 |
≥ 2.5 |
— |
(JP5000 & JP8000, DJ2600 & DJ2700, JetKote, Woka Jet, K2)
|
ZTC4953D |
– 45 + 20 |
≥ 2.5 |
— |
||
ZTC4952D |
– 45 + 15 |
≥ 2.5 |
— |
||
ZTC4981D |
– 45 + 11 |
≥ 2.5 |
— |
||
ZTC4954D |
– 38 + 10 |
≥ 2.5 |
— |
||
ZTC4982D |
– 30 + 10 |
≥ 2.5 |
— |
||
We can tailor-make different particle size distributions and apparent densities for various applications. |
Recommended Spray Parameters (HVOF) |
|
Coating Properties |
||
Material |
Cr3C2 – 37WC – 18NiCoCr |
|
Hardness (HV0.3) |
1050 – 1250 |
Manufacturing |
Agglomerated & Sintered |
|
Bonding Strength (MPa) |
> 60MPa |
Size Fraction (µm) |
– 45 + 15 |
|
Deposited efficiency (%) |
40 – 48% |
Spray Torch |
JP5000 |
|
Porosity (%) |
< 3% |
Nozzle (inch) |
6 |
|
|
|
Kerosene (L/h) |
25 |
|
||
Oxygen (L/min) |
900 |
|
||
Carrier gas (Ar) (L/min) |
7.5 |
|
||
Powder feed rate (g/min) |
70 – 80 |
|
||
Spraying distance (mm) |
320 – 380 |
|