WC-20Cr3C2-7Ni थर्मल स्प्रे पाउडर
- Agglomerated and sintered gray-black spherical or near-spherical particles with good flowability.
- The maximum service temperature is up to 750℃. It can be used in humid environments.
- The dense coating has excellent resistance to oxidation, corrosion, and abrasion.
- Anti-oxidation and corrosion resistance are better than WC-Co – based coatings.
- Mainly used in the steel & iron industry, paper making, pump valves, etc.
ग्रेड र रासायनिक संरचना
ग्रेड |
रासायनिक संरचना (Wt, %) |
|||||
डब्लु |
T. C |
नि |
Cr |
फे |
ओ |
|
ZTC48D* |
सन्तुलन |
5.8 – 6.4 |
6 – 8 |
20 – 23 |
≤ ०.५ |
≤ ०.५ |
*: D stands for spherical or nearly spherical thermal spray powder.
आकार र भौतिक गुणहरू
ग्रेड |
टाइप गर्नुहोस् |
आकार अंश (μm) |
स्पष्ट घनत्व (g/cm³) |
बग्ने गति (s/50g) |
आवेदन |
ZTC4851D |
WC – Cr3सी2 – Ni 73/20/7 Agglomerated सिन्टर्ड |
– 53 + 20 |
≥ ४ |
≤ १८ |
(JP5000 & JP8000, DJ2600 & DJ2700, JetKote, वोका जेट, K2)
|
ZTC4853D |
– 45 + 20 |
≥ ४ |
≤ १८ |
||
ZTC4852D |
– 45 + 15 |
≥ ४ |
≤ १८ |
||
ZTC4881D |
– 45 + 11 |
≥ ४ |
≤ १८ |
||
ZTC4854D |
– 38 + 10 |
≥ ४ |
≤ १८ |
||
ZTC4882D |
– 30 + 10 |
≥ ४ |
≤ ३० |
||
हामी विभिन्न अनुप्रयोगहरूको लागि विभिन्न कण आकार वितरण र स्पष्ट घनत्व दर्जी बनाउन सक्छौं। |
सिफारिस गरिएको स्प्रे प्यारामिटरहरू (HVOF) |
|
कोटिंग गुणहरू |
||
सामग्री |
WC -20Cr3सी2 – 7Ni |
|
कठोरता (HV0.3) |
950 – 1200 |
निर्माण |
एग्लोमेरेटेड र सिंटर गरिएको |
|
बन्धन बल (MPa) |
> 70MPa |
आकार अंश ( µm ) |
– 45 + 15 |
|
निक्षेप दक्षता (%) |
35 – 45% |
टर्च स्प्रे |
JP5000 |
|
पोरोसिटी (%) |
<1% |
नोजल (इन्च) |
6 |
|
|
|
केरोसिन (L/h) |
23 |
|
||
अक्सिजन (L/min) |
900 |
|
||
क्यारियर ग्यास (Ar) (L/min) |
8.0 |
|
||
पाउडर फिड दर (g/min) |
70 – 80 |
|
||
स्प्रे गर्ने दूरी (मिमी) |
340 – 360 |
|