WC-20Cr3C2-7Ni termisk spraypulver
- Agglomerated and sintered gray-black spherical or near-spherical particles with good flowability.
- The maximum service temperature is up to 750℃. It can be used in humid environments.
- The dense coating has excellent resistance to oxidation, corrosion, and abrasion.
- Anti-oxidation and corrosion resistance are better than WC-Co – based coatings.
- Mainly used in the steel & iron industry, paper making, pump valves, etc.
Karakter og kjemisk sammensetning
Karakter |
Kjemisk sammensetning (Wt, %) |
|||||
W |
T.C |
Ni |
Cr |
Fe |
O |
|
ZTC48D* |
Balansere |
5.8 – 6.4 |
6 – 8 |
20 – 23 |
≤ 0,5 |
≤ 0,5 |
*: D stands for spherical or nearly spherical thermal spray powder.
Størrelse og fysiske egenskaper
Karakter |
Type |
Størrelsesbrøk (μm) |
Tilsynelatende tetthet ( g/cm³) |
Strømningshastighet (s/50g) |
applikasjon |
ZTC4851D |
WC – Cr3C2 – Ni 73/20/7 Agglomerated & Sintret |
– 53 + 20 |
≥ 4 |
≤ 18 |
(JP5000 & JP8000, DJ2600 & DJ2700, JetKote, Woka Jet, K2)
|
ZTC4853D |
– 45 + 20 |
≥ 4 |
≤ 18 |
||
ZTC4852D |
– 45 + 15 |
≥ 4 |
≤ 18 |
||
ZTC4881D |
– 45 + 11 |
≥ 4 |
≤ 18 |
||
ZTC4854D |
– 38 + 10 |
≥ 4 |
≤ 18 |
||
ZTC4882D |
– 30 + 10 |
≥ 4 |
≤ 30 |
||
Vi kan skreddersy ulike partikkelstørrelsesfordelinger og tilsynelatende tettheter for ulike bruksområder. |
Anbefalte sprayparametre (HVOF) |
|
Beleggegenskaper |
||
Materiale |
WC -20Cr3C2 – 7Ni |
|
Hardhet (HV0.3) |
950 – 1200 |
Produksjon |
Agglomerert og sintret |
|
Bindingsstyrke (MPa) |
> 70 MPa |
Størrelsesbrøk ( µm ) |
– 45 + 15 |
|
Avsatt effektivitet (%) |
35 – 45% |
Spray lommelykt |
JP5000 |
|
Porøsitet (%) |
< 1% |
Munnstykke (tommer) |
6 |
|
|
|
Parafin (L/t) |
23 |
|
||
Oksygen (l/min) |
900 |
|
||
Bæregass (Ar) (L/min) |
8.0 |
|
||
Pulvermatingshastighet (g/min) |
70 – 80 |
|
||
Sprøyteavstand (mm) |
340 – 360 |
|