WC-20Cr3C2-7Ni Thermal Spray Powder
- Agglomerated and sintered gray-black spherical or near-spherical particles with good flowability.
- The maximum service temperature is up to 750℃. It can be used in humid environments.
- The dense coating has excellent resistance to oxidation, corrosion, and abrasion.
- Anti-oxidation and corrosion resistance are better than WC-Co – based coatings.
- Mainly used in the steel & iron industry, paper making, pump valves, etc.
Одделение и хемиски состав
Одделение |
Хемиски состав (Wt, %) |
|||||
В |
Т.Ц |
Ни |
Кр |
Fe |
О |
|
ZTC48D* |
Биланс |
5.8 – 6.4 |
6 – 8 |
20 – 23 |
≤ 0,5 |
≤ 0,5 |
*: D stands for spherical or nearly spherical thermal spray powder.
Size и физички својства
Одделение |
Тип |
Дропка на големина (μm) |
Очигледна густина (g/cm³) |
Проток (s/50g) |
Апликација |
ZTC4851D |
WC – Cr3В2 – Ni 73/20/7 Agglomerated &Синтерувано |
– 53 + 20 |
≥ 4 |
≤ 18 |
(JP5000 & JP8000, DJ2600 & DJ2700, JetKote, Вока Џет, К2)
|
ZTC4853D |
– 45 + 20 |
≥ 4 |
≤ 18 |
||
ZTC4852D |
– 45 + 15 |
≥ 4 |
≤ 18 |
||
ZTC4881D |
– 45 + 11 |
≥ 4 |
≤ 18 |
||
ZTC4854D |
– 38 + 10 |
≥ 4 |
≤ 18 |
||
ZTC4882D |
– 30 + 10 |
≥ 4 |
≤ 30 |
||
Можеме да направиме различни распределби на големината на честичките и очигледни густини за различни апликации. |
Препорачани параметри за прскање (HVOF) |
|
Својства на обложување |
||
Материјал |
WC -20Cr3В2 – 7Ni |
|
Цврстина (HV0.3) |
950 – 1200 |
Производство |
Агломерирани и синтерувани |
|
Јачина на врзување (MPa) |
> 70 MPa |
Дропка на големина ( μm ) |
– 45 + 15 |
|
Депонирана ефикасност (%) |
35 – 45% |
Спреј факел |
JP5000 |
|
Порозност (%) |
< 1% |
Млазница (инчи) |
6 |
|
|
|
Керозин (L/h) |
23 |
|
||
Кислород (L/min) |
900 |
|
||
Носечки гас (Ar) (L/min) |
8.0 |
|
||
Стапка на напојување во прав (g/min) |
70 – 80 |
|
||
Растојание на прскање (мм) |
340 – 360 |
|