WC-20Cr3C2-7Ni lämpösuihkejauhe
- Agglomerated and sintered gray-black spherical or near-spherical particles with good flowability.
- The maximum service temperature is up to 750℃. It can be used in humid environments.
- The dense coating has excellent resistance to oxidation, corrosion, and abrasion.
- Anti-oxidation and corrosion resistance are better than WC-Co – based coatings.
- Mainly used in the steel & iron industry, paper making, pump valves, etc.
Laatu ja kemiallinen koostumus
Arvosana |
Kemiallinen koostumus (Wt, %) |
|||||
W |
T. C |
Ni |
Cr |
Fe |
O |
|
ZTC48D* |
Saldo |
5.8 – 6.4 |
6 – 8 |
20 – 23 |
≤ 0,5 |
≤ 0,5 |
*: D stands for spherical or nearly spherical thermal spray powder.
S ize & Fyysiset ominaisuudet
Arvosana |
Tyyppi |
Koko murto-osa (μm) |
Näennäinen tiheys ( g/cm³) |
Virtausnopeus (s/50g) |
Sovellus |
ZTC4851D |
WC – Cr3C2 – Ni 73/20/7 Agglomerated & Sintrattu |
– 53 + 20 |
≥ 4 |
≤ 18 |
(JP5000 & JP8000, DJ2600 & DJ2700, JetKote, Woka Jet, K2)
|
ZTC4853D |
– 45 + 20 |
≥ 4 |
≤ 18 |
||
ZTC4852D |
– 45 + 15 |
≥ 4 |
≤ 18 |
||
ZTC4881D |
– 45 + 11 |
≥ 4 |
≤ 18 |
||
ZTC4854D |
– 38 + 10 |
≥ 4 |
≤ 18 |
||
ZTC4882D |
– 30 + 10 |
≥ 4 |
≤ 30 |
||
Voimme räätälöidä erilaisia hiukkaskokojakaumia ja näennäisiä tiheyksiä eri sovelluksiin. |
Suositellut ruiskutusparametrit (HVOF) |
|
Pinnoitteen ominaisuudet |
||
Materiaali |
WC -20Cr3C2 – 7Ni |
|
Kovuus (HV0.3) |
950 – 1200 |
Valmistus |
Agglomeroitu ja sintrattu |
|
Liimauslujuus (MPa) |
> 70 MPa |
Kokofraktio ( µm ) |
– 45 + 15 |
|
Talletettu tehokkuus (%) |
35 – 45% |
Spray taskulamppu |
JP5000 |
|
Huokoisuus (%) |
< 1% |
Suutin (tuumaa) |
6 |
|
|
|
Kerosiini (l/h) |
23 |
|
||
Happi (l/min) |
900 |
|
||
Kantokaasu (Ar) (l/min) |
8.0 |
|
||
Jauheen syöttönopeus (g/min) |
70 – 80 |
|
||
Ruiskutusetäisyys (mm) |
340 – 360 |
|