WC-20Cr3C2-7Ni Thermal Spray Powder

  • Agglomerated and sintered gray-black spherical or near-spherical particles with good flowability.
  • The maximum service temperature is up to 750℃. It can be used in humid environments.
  • The dense coating has excellent resistance to oxidation, corrosion, and abrasion.
  • Anti-oxidation and corrosion resistance are better than WC-Co – based coatings.
  • Mainly used in the steel & iron industry, paper making, pump valves, etc.

Kvalitet og kemisk sammensætning

karakter

Kemisk sammensætning (Wt, %)

W

T.C 

Ni

Cr

Fe

O

ZTC48D*

Balance

5.8 – 6.4

6 – 8

20 – 23

≤ 0,5

≤ 0,5

*: D stands for spherical or nearly spherical thermal spray powder.

Størrelse & fysiske egenskaber

karakter

Type

Størrelsesbrøk (μm)

Tilsyneladende massefylde (g/cm³)

Strømningshastighed

(s/50g)

Ansøgning

ZTC4851D

WC – Cr3C2 – Ni

73/20/7 Agglomerated

& Sintret

– 53 + 20

≥ 4

≤ 18
  • HVOF

(JP5000 & JP8000, DJ2600 & DJ2700, JetKote,

Woka Jet, K2)

  • HVAF
  • APS

ZTC4853D

– 45 + 20

≥ 4

≤ 18

ZTC4852D

– 45 + 15

≥ 4

≤ 18

ZTC4881D

– 45 + 11

≥ 4

≤ 18

ZTC4854D

– 38 + 10

≥ 4

≤ 18

ZTC4882D

– 30 + 10

≥ 4

≤ 30
Vi kan skræddersy forskellige partikelstørrelsesfordelinger og tilsyneladende tætheder til forskellige applikationer.
Anbefalede sprøjteparametre (HVOF)

Belægningsegenskaber
Materiale

WC -20Cr3C2 – 7Ni

Hårdhed (HV0.3)

950 – 1200
Fremstilling

Agglomereret og sintret

Bindingsstyrke (MPa)

> 70 MPa
Størrelsesbrøk ( µm )

– 45 + 15

Deponeret effektivitet (%)

35 – 45%
Spray lommelygte

JP5000

Porøsitet (%)

< 1%
Dyse (tommer)

6

Petroleum (L/h)

23

Ilt (L/min)

900

Bæregas (Ar) (L/min)

8.0

Pulvertilførselshastighed (g/min)

70 – 80

Sprøjteafstand (mm)

340 – 360